Smith Wesson 642 小左轮，银色枪身，扳机像是烧焦了的废旧零件

easycity

今天才拿到Smith Wesson 642 小左轮，银色枪身，非常漂亮。再一细看，扳机像是烧焦了的废旧零件。当时就想大骂网店是奸商，把一支烧毁了的枪当作新枪卖给我。回来仔细审视，发现其他地方都是亮闪闪的，一点使用的痕迹都没有。上官网一查，发现642就是这个德行，而亮闪闪的扳机作为一个选项，只出现在更昂贵的型号上。现在我是要骂Smith Wesson是奸商了，故意恶心消费者。





有没有原厂的Chrome-Plated， Polished 扳机我可以直接换上去？
或者有没有化学试剂我可以处理，就像烤蓝或者镀铬，而且经得起磨损？
如果直接把表面烧灼的痕迹用砂纸打磨掉，会有什么不利影响，会是什么外观效果？
不过，三百出头一点的价格，功能没有问题，就物超所值了。看看自己动手能够改善到什么地步。

kenshiro

时间久了你还会发现，这扳机不光难看，还容易生锈

taurus

https://www.youtube.com/watch?v=I4GtXq2XXOI

bearlck

S&W的左轮从98年左右就全面切换成MIM扳机了，过了1年左右，HAMMER也切换成MIM部件了

neotsu

我们常常说，光有了枪是不行的，你还要常常用。
其实脑子也一样。

楼主可以找一下sw早期良心尚存版本，都是亮闪闪的，很难，存世数量不多。

因为亮闪闪，hammer软，所以。。这些“良心”版本大部分被弃用、召回了

祝楼主好运哦。

Tank-Tank

这是淬火过， 为了增加强度。 sw左轮全部这样。

Snowbird

楼上说的是正解，这个是热处理后的样子。

easycity

谢谢各位的解释。
我会注意防锈。
金属部件热处理应该是比较常见的，但是跟镀铬这样的美化外观的设计应该没有冲突。Smith就像是故意省了一道工序，把外观破坏掉，恶心那些购买基本版的消费者。
我自己试着镀铬或者烤蓝，慢慢来。即使不成功，也不过就是原来的样子。

X-PGH

https://www.calguns.net/calgunforum/showthread.php?t=1250034

热处理, - Case Hardening - 之后 SW "省工省钱", 略去表面再处理.

其他一些厂家的 Revolvers - Triggers are much better looking.

oldben

可以用细砂纸把表面打磨一下 ，先用1000左右的，然后用2000 或更细的。

电镀之后表面还要抛光，才会亮闪闪的。

大番茄

你手里的438扳机不应该跟这把是一样的么?

easycity

大番茄 发表于 2020-5-19 06:15
你手里的438扳机不应该跟这把是一样的么?

刚才看了一下438的扳机，也有烧烤的痕迹，不过好像还有一层烤蓝一样的表面工艺，不仔细看，与枪身的外观没有差别，所以我打了至少几百发，都没有发现扳机的外观有什么异样。642的枪身太漂亮了，扳机也没有任何表面工艺修饰，反差太大。不过，网上好像也没有人介绍如何镀铬，应该是习惯了。我也可以先打个几百发，看能不能习惯这个另类审美观。

双筒

说case hardening的其实那是以前。 我的翻译：史外甥以前是用case hardening来增加击锤和扳机的表面硬度，延长寿命。 当2-30年代廉价的西班牙左轮来竞争的时候，史外甥为了让他们的枪一眼就能看出去跟那些便宜山寨货的不同，他们把这个“烧焦了”的颜色给注册成商标了，这样如果西班牙的枪也用case hardening，那将会是商标侵权；如果不用那一眼就能看出来不同。 现在史外甥用的是MIM金属射出成型的技术，扳机硬度已经是里外都一样高了，无需case hardening了，但他们的注册商标还是要维持（商标和专利不一样，不会自动作废，但不再用了就作废），所以他们用staining染色的办法让扳机和击锤还看上去像做了case hardening的样子，烧焦了的。链接见下：

For a century or more, S&W used color case hardening on its hammers and triggers so they would not wear out and would keep the fine edges needed for a good trigger pull, while retaining a softer center that would be durable overall.

When cheap Spanish imitations of the S&W were imported in the 1920's and 1930's, one way S&W took to keep the foreign guns from being passed off as S&W's was to trademark that coloring. If the Spanish makers copied the coloring, their guns could be banned from import for a trademark violation; if they didn't, their guns would not look like S&W's.

But when S&W went to MIM parts, case hardening was no longer needed; the MIM parts are hard all the way through. But S&W wanted to retain the colored hammer and trigger because they are trademarked, so they took to staining the parts. (A patent expires; a trademark does not, unless a company stops using it, so S&W had to keep using colored hammers and triggers on at least some guns.)

https://thefiringline.com/forums/showthread.php?t=542411

maomaochong

Tank-Tank 发表于 2020-5-18 19:52
这是淬火过， 为了增加强度。 sw左轮全部这样。

maomaochong

Beautiful

Snowbird

双筒 发表于 2020-5-19 08:23
说case hardening的其实那是以前。 我的翻译：史外甥以前是用case hardening来增加击锤和扳机的表面硬度， ...

涨姿势了，没想到还有这个变故

easycity

双筒 发表于 2020-5-19 08:23
说case hardening的其实那是以前。 我的翻译：史外甥以前是用case hardening来增加击锤和扳机的表面硬度， ...

原来还有这个典故！
我差点费钱费力，把高档的Smith Wesson百年经典，烧烤扳机，降格成了亮闪闪扳机的地摊货。
谢谢科普！

大番茄

双筒 发表于 2020-5-19 11:23
说case hardening的其实那是以前。 我的翻译：史外甥以前是用case hardening来增加击锤和扳机的表面硬度， ...

学到了

双筒

回楼上几位弟兄：没问题，我也是刚学到的，现学现卖。 而且还头一次听说商标也会作废，一直以为商标注册了就是你的了，爱怎么用怎么用，就像公民拿到了爱住哪儿没人管。 现在看这是更像绿卡，拿了不在米国呆足够时间人要收回去的。 想想也是有道理，商标拿了又不用就跟占着茅坑不拉屎的，比较让人烦。。。

neotsu

双筒 发表于 2020-5-19 08:23
说case hardening的其实那是以前。 我的翻译：史外甥以前是用case hardening来增加击锤和扳机的表面硬度， ...

嗯，而且MIM不是什么小厂都能做的，试错成本很高，随便作废一批就赔了。所以有些厂家用MIM件都是委外做的。

所以上来就痛骂SW是奸商，真是有脑筋有知识，还有一腔正义感呢。